02811cas a2200409 a 4500 20260817161352.0 110920s1989 th uu|m rtt 0| a1eng d .b1005070x AIT Thesis no.AE-89-05 Tamtomo, Pontianus Accelerated wear testing of enamel coatings Bangkok : Asian Institute of Technology, 1989 115 p. Thesis ; no. AE-89-05 A thesis submitted in partial fulfillment of the requirements for the degree of Master of Engineering, School of Environment, Resources and Development Thesis (M. Eng.) - Asian Institute of Technology, 1989 Accelerated wear testing of enamel coating on mild steel rings was conducted to investigate the wear characteristics of enamel coating . These wear tests were conducted in sandy soil and on sand papers and the performance of enamel was compared with the mild steel. Results of the study are given in terms of weight loss and wear rate due to abrasion in relation to the duration. The amount of wear and the wear rate of enel coated ring were almost the same as the uncoated mild steel ring in sandy soil. However on the sand paper no. 120 and no. 100 the enamel coated rings showed more wear than the mild steel. Based on the studies conducted it was roughly estimated that the enamel coating should last for at least 80 ha of cultivation or 8 years of service life. The weathering studies of enamel coated plates showed that enamel coated ring is an excellent weatherproof material. Based on the results in this study it could be concluded that enamel coating has sufficient wear resistance and should be used on cage wheel lugs or other agricultural implement. Mechanical wear Agricultural machinery Salokhe, Vilas M., Chairperson Singh, Gajendra, Examination Committee Gee-Clough, D., Examination Committee Gupta, Chandra P., Examination Committee US-ASEAN, Scholarship Donor Asian Institute of Technology. Thesis ; no. AE-89-05 Full-Text http://203.159.5.9/ait-thesis/detail.php?q=B17817 .b1005070x mnait s 240409 2 951012 m a s 0 mnait mnarc 22 40 Barcode : 30050120581722 CREATED : 2014-10-02 RECORD # : i12760201 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 Barcode : 30050120364194 CREATED : 2016-05-27 RECORD # : i12997407 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 1036 1036 0 0 0 0 MAIN MAIN mnait 2026-08-17 50.00 0 AIT Thesis no.AE-89-05 30050120581722 2026-08-17 16:13:52 3 2026-08-17 22 0 0 0 0 MAIN MAIN mnarc 2026-08-17 0 AIT Thesis no.AE-89-05 30050120364194 2026-08-17 16:13:52 2026-08-17 40