03089nas|a2200421 i 4500 20260818100027.0 181199s1999 th uu m rtt 00| a1eng d .b11764909 AIT Thesis no. GE-98-06 Tun Lwin Engineering properties of cement treated Bangkok clay Bangkok : Asian Institute of Technology, 1999 112 leaves Thesis ; no. GE-98-06 A thesis submitted in partial fulfillment of the requirements for the degree of Master of Science, School of Civil Engineering Thesis (M.Sc.) - Asian Institute of Technology, 1999 Strength, compressibility, permeability and creep behavior of cement treated Bangkok clay was investigated. Soil samples were taken from Bangplee site. The clay sample was thoroughly mixed with Portland cement (Type I), using a special mixing and molding procedure to ensure uniformity of specimen. At 28 days, strength of cement treated clay was found 20 times higher than that of the base clay. Axial strain decreased with an increase in cement content. The stress path of cement treated clay was similar to that of highly overconsolidated clay. Effective friction angle increased with cement content. The cement treated clal showed lower friction angle as the cement content increased more than 150 kg/m . Cohesion intercept increased with cement content. Preconsolidation pressure increased with an increase in cement content. Permeability of cement treated clay was decreased with an increase in cement content. During undrained creep test, small axial deformation was found. Pore pressure increased with time under constant stress level. Semple's (1973) exponential creep equation is applicable for undrained creep behavior of cement treated Bangkok clay. Clay Thailand Bangkok Soil mechanics Thailand Bangkok Noppadol Phien-Wej, Chairperson Der Guey, Lin, Chairperson Bergado, Dennes T., Examination Committee Asian Institute of Technology (Partial), Scholarship donor Asian Institute of Technology. Thesis ; no. GE-98-06 Full-Text http://203.159.5.9/ait-thesis/detail.php?q=B12424 .b11764909 mnait y 240420 0 991112 m a y 0 mnait mnait mnarc 20 40 Barcode : 30050120717458 CREATED : 1998-06-15 RECORD # : i12162528 LPATRON : 1016810 LCHKIN : 2006-05-21 # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 1 TOT CHKOUT : 4 TOT RENEW : 0 Barcode : 30050120717425 CREATED : 1998-06-15 RECORD # : i1216253x LPATRON : 1030128 LCHKIN : 2020-02-11 # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 10 TOT RENEW : 4 Barcode : 30050160080650 CREATED : 2016-05-17 RECORD # : i12979648 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 38213 38213 0 0 0 0 MAIN MAIN mnait 2026-08-18 50.00 0 AIT Thesis no. GE-98-06 30050120717458 2026-08-18 10:00:27 1 2026-08-18 20 0 0 0 0 MAIN MAIN mnait 2026-08-18 50.00 0 AIT Thesis no. GE-98-06 30050120717425 2026-08-18 10:00:27 2 2026-08-18 20 0 0 0 0 MAIN MAIN mnarc 2026-08-18 0 AIT Thesis no. GE-98-06 30050160080650 2026-08-18 10:00:27 1 2026-08-18 40