04834nas a2200481 a 4500 20260818113223.0 190826s2017 th uu m rtt 0| a1eng d .b12310025 AIT Thesis no.FB-17-01 Shrestha, Pratiksha Extraction of crystalline nanocellulose from banana pseudostems and its utilization in developing bio-nanocomposite film Pathum Thani, Thailand : Asian Institute of Technology, 2017 78 leaves : ill. + 1 online resource Thesis ; no.FB-17-01 A thesis submitted in partial fulfillment of the requirements for the degree of Master of Science in Food Engineering and Bioprocess Technology, School of Environment, Resources and Development Thesis (M. Sc.) - Asian Institute of Technology, 2017 Lignocellulosic agricultural residue is one of the cheapest source of cellulose based biomaterial. Myriad of research have been conducted on extraction of crystalline nanocellulose and its characterization but only little is known about its drug binding ch emistry and chemical modifications limiting its utilization in biomedical applications. In this work crystalline nanocellulose (CNC) was isolated from banana pseudostem waste by acid hydrolysis method and tetracycline (TC) loaded nanocomposite was develope d by crosslinking with Butane tetra carboxylic acid ( BTCA ) and chitosan. Thus obtained CNCs were found to have have nanoscopic dimension (18.79±5.30 nm diameter and 202.12±37.43 nm length) and exhibited high degree of crystallinity (81.67%). Morpholog ical study and chemical characterization of CNCs were performed by Scanning Electron Microscopy (SEM), Fourier Transmission Infra - Red (FT - IR) spectroscopy , Thermo gravimetric analysis (TGA) and X - Ray Diffraction (XRD). Nanocomposites were prepared by four diffe rent modification methods by crosslinking with BTCA and varying concentration of TC and chitosa n. Films (0.18 ± 0.01 mm) prepared by solvent evaporation method were casted in acrylic plates and film morphology, mechanical properties and thermal behavior w ere studied. In vitro release of TC was carried in citrate buffer (pH 5.7) at incubating condition (37 C̊) with constant stirring (100 rpm) and sustained release of up to 16 h was observed with TC loaded nanocomposite film with modification method 3. Antiba cterial propert ies of nanocomposite film against Gram - positive ( Staphylococcus aureus ) and Gram - negative ( Escherichia coli ) was investigated. Nanocomposite film (25 mm diameter) with modification method 3 showed highest zone of inhibition for both E. coli (36.3 ± 0.6 mm) and Staph. aureus (39.3 ± 0.6 mm) with TC drug loading (1205 og) and crosslinking with chitosan. The obtained nanocomposite can potentially be applied in biomedical field for efficient drug delivery and developing transdermal patches. Findi ng of the present study reveals economic production of biomaterial for medical applications utilizing lignocellulosic waste. Nanocomposites (Materials) Cellulose Biotechnology Crystalline polymers Anal, Anil Kumar, Chairperson Nguyen, Loc Thai, Examination committee Sadiq, Muhammad Bilal, Examination committee Thailand (HM Queen), Scholarship donor Asian Institute of Technology. Thesis ; no. no.FB-17-01 Full-Text http://203.159.5.9/ait-thesis/detail.php?q=B02860 .b12310025 mnait m 240925 0 190826 m a m 0 000:001:PDF:b1231002:004333:0:0:0:0:0:0 Click to view Abstract n mnait mnait mnarc mnarc 40 61 20 Barcode : 30050120894463 CREATED : 2019-05-23 RECORD # : i13188434 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 Barcode : - CREATED : 2019-05-23 RECORD # : i13188446 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 Barcode : 30050120955595 CREATED : 2019-08-26 RECORD # : i13213714 LPATRON : 1028262 LCHKIN : 2020-05-01 # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 1 TOT RENEW : 1 Barcode : 30050120955561 CREATED : 2019-08-26 RECORD # : i13213726 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 42669 42669 0 0 0 0 MAIN MAIN mnarc 2026-08-18 0 AIT Thesis no.FB-17-01 30050120894463 2026-08-18 11:32:23 1 2026-08-18 40 0 0 0 0 MAIN MAIN mnarc 2026-08-18 0 AIT Thesis no.FB-17-01 2026-08-18 11:32:23 2026-08-18 61 0 0 0 0 MAIN MAIN mnait 2026-08-18 50.00 0 AIT Thesis no.FB-17-01 30050120955595 2026-08-18 11:32:23 1 2026-08-18 20 0 0 0 0 MAIN MAIN mnait 2026-08-18 50.00 0 AIT Thesis no.FB-17-01 30050120955561 2026-08-18 11:32:23 2 2026-08-18 20