02959nam a2200409 4500 20260818113516.0 290798 th eng .b10273219 AIT Thesis no. ST-89-11 Jiranan Prakopvitayakit Fatigue strength of orthotropic steel bridge deck paved with epoxy asphaltic concrete Bangkok : Asian Institute of Technology, 1989 61 p. Thesis ; no. ST-89-11 A thesis submitted in partial fulfillment for the requirements of the degree of Master of Engineering, School of Engineering and Technolog Thesis (M.Eng.) - Asian Institute of Technology, 1989 An experimental investigation was conducted to evaluate the performance of an orthotropic steel bridge deck paved with epoxy asphaltic concrete subjected to a repetition cyclic load. It involved; the use and mixing procedure of epoxy asphaltic concrete on steel plate and determination of a suitable mix proportion for use in paving orthotropic steel bridge deck. An S - N curve, for the orthotropic steel bridge deck paved with epoxy asphaltic concrete was experimentally developed. The test results indicate that: epoxy asphaltic concrete which contains local aggregate has an average percent air void less than that required by the manufacturer. The S - N curve of steel plates paved with epoxy asphaltic concrete is developed between the range of 15 to 30% of the ultimate load. Two modes of failure were observed. The five tested specimens failed because of tension cracks originating in the top fiber of the epoxy asphaltic concrete. In one specimen there was a combination of cracking in the top fiber and bond failure at the interface. Bridges, Steel plate deck Bridges, Concrete Testing Pichai Nimityongskul, Chairperson Karasudhi, Pisidhi, Examination Committee Ueda, Tamon, Examination Committee Asian Institute of Technology. Thesis ; no. ST-89-11 Full-Text http://203.159.5.9/ait-thesis/detail.php?q=B18123 .b10273219 mnait s 240401 2 951012 m a s 0 mnait mnait mnarc 20 40 Barcode : 30050003064283 CREATED : 1995-10-14 RECORD # : i10336916 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 Barcode : 30050003064275 CREATED : 1995-10-14 RECORD # : i10336928 LPATRON : 1019508 LCHKIN : 2008-08-19 # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 1 TOT RENEW : 0 Barcode : 30050160068754 CREATED : 2016-08-04 RECORD # : i12932097 LPATRON : 0 LCHKIN : - # RENEWALS : 0 # OVERDUE : 0 IUSE3 : 0 TOT CHKOUT : 0 TOT RENEW : 0 43516 43516 0 0 0 0 MAIN MAIN mnait 2026-08-18 0 AIT Thesis no. ST-89-11 30050003064283 2026-08-18 11:35:16 1 2026-08-18 20 0 0 0 0 MAIN MAIN mnait 2026-08-18 0 AIT Thesis no. ST-89-11 30050003064275 2026-08-18 11:35:16 2 2026-08-18 20 0 0 0 0 MAIN MAIN mnarc 2026-08-18 0 AIT Thesis no. ST-89-11 30050160068754 2026-08-18 11:35:16 1 2026-08-18 40